PubMed İndeksli Yayınlar Koleksiyonu
Permanent URI for this collectionhttps://hdl.handle.net/20.500.12416/8650
Browse
Search Results
Article Citation - WoS: 31Citation - Scopus: 32A Comparative Study on Biodegradation and Mechanical Properties of Pressureless Infiltrated Ti/Ti6al4v-mg Composites(Elsevier Science Bv, 2016) Karakas, M. Serdar; Esen, Ziya; Butev, EzgiThe mechanical response and biodegradation behavior of pressureless Mg-infiltrated Ti-Mg and Ti6Al4V-Mg composites were investigated by compression and simulated body fluid immersion tests, respectively. Prior porous preforms were surrounded uniformly with magnesium as a result of infiltration and the resultant composites were free of secondary phases and intermetallics. Although the composites' compressive strengths were superior compared to bone, both displayed elastic moduli similar to that of cortical bone and had higher ductility with respect to their starting porous forms. However, Ti-Mg composites were unable to preserve their mechanical stabilities during in-vitro tests such that they fractured in multiple locations within 15 days of immersion. The pressure generated by H-2 due to rapid corrosion of magnesium caused failure of the Ti-Mg composites through sintering necks. On the other hand, the galvanic effect seen in Ti6Al4V-Mg was less severe compared to that of Ti-Mg. The degradation rate of magnesium in Ti6Al4V-Mg was slower, and the composites were observed to be mechanically stable and preserved their integrities over the entire 25-day immersion test. Both composites showed bioinert and biodegradable characteristics during immersion tests and magnesium preferentially corroded leaving porosity behind while Ti/Ti6Al4V remained as a permanent scaffold. The porosity created by degradation of magnesium was refilled by new globular agglomerates. Mg(OH)(2) and CaHPO4 phases were encountered during immersion tests while MgCl2 was detected during only the first 5 days. Both composites were classified as bioactive since the precipitation of CaHPO4 phase is known to be precursor of hydroxyapatite formation, an essential requirement for an artificial material to bond to living bone. (C) 2016 Elsevier Ltd. All rights reserved.Article Citation - WoS: 15Citation - Scopus: 17Characterization of Ti6al7nb Alloy Foams Surface Treated in Aqueous Naoh and Cacl2 Solutions(Elsevier Science Bv, 2016) Esen, Ziya; Bor, Sakir; Butev, EzgiTi6Al7Nb alloy foams having 53-73% porosity were manufactured via evaporation of magnesium space holders. A bioactive 1 mu m thick sodium hydrogel titanate layer, NaxH2-xTiyO2y+1., formed after 5 M NaOH treatment, was converted to crystalline sodium titanate, Na2TiyO2y+1, as a result of post-heat treatment. On the other hand, subsequent CaCl2 treatment of NaOH treated specimens induced calcium titanate formation. However, heat treatment of NaOH-CaCl2 treated specimens led to the loss of calcium and disappearance of the titanate phase. All of the aforementioned surface treatments reduced yield strengths due to the oxidation of the cell walls of the foams, while elastic moduli remained mostly unchanged. Accordingly, equiaxed dimples seen on the fracture surfaces of as-manufactured foams turned into relatively flat and featureless fracture surfaces after surface treatments. On the other hand, Ca- and Na-rich coating preserved their mechanical stabilities and did not spall during fracture. The relation between mechanical properties of foams and macro-porosity fraction were found to obey a power law. The foams with 63 and 73% porosity met the desired biocompatibility requirements with fully open pore structures and elastic moduli similar to that of bone. In vitro tests conducted in simulated body fluid (SBF) showed that NaOH-heat treated surfaces exhibit the highest bioactivity and allow the formation of Ca-P rich phases having Ca/P ratio of 1.3 to form within 5 days. Although Ca-P rich phases formed only after 15 days on NaOH-CaCl2 treated specimens, the Ca/P ratio was closer to that of apatite found in bone. (C) 2016 Elsevier Ltd. All rights reserved.